- Preparation for WC-Ni<sub>3</sub>Al Hard Metal by Vacuum Sintering
- 真空焼結によるWC-Ni₃Al超硬合金の作製
- シンクウ ショウケツ ニ ヨル WC-Ni ₃ Al チョウコウゴウキン ノ サクセイ
この論文をさがす
説明
<p>WC-Ni3Al hard metal of the composition for WC-25 vol% (Ni-24 at%Al-0.5 at%B) was prepared by vacuum sintering. The powder mixtures of WC, Ni, NiAl (Ni-50 at%Al) and B were treated by wet milling with tumbling ball mill machine for 24 hr and 48 hr. The average particle size of the powder mixtures after wet-milling for 24 hr and 48 hr were 1.69 μm and 1.23 μm, respectively. These powder mixtures were press-molded into the test-piece and sintered in vacuum of (7~9) × 10−3 Pa at various temperature for 1 hr. The densities, microstructures and mechanical properties of the obtained sintered compacts were investigated. When 48 hr wet-milled powder was used and the green compact was sintered at 1425°C for 1 hr, the compact had a relative density more than 99%, transverse rapture strength of 2.2 GPa and vickers hardness of 1330 HV. On the other hand, using 24 hr wet-milled powder, the sintered compact had lower mechanical properties than the compact of 48 hr wet-milled powder due to low density and inhomogeneous microstructure.</p>
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 64 (11), 615-620, 2017
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681287211904
-
- NII論文ID
- 130006224973
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 028702262
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可