- Effect of Oxygen-enriched h-BN Powder on the Property of h-BN/Feldspar Composite
- h-BN/長石-複合焼結体の特性に及ぼす高酸素含有h-BN粉末使用の効果
- h-BN/チョウセキ-フクゴウ ショウケツタイ ノ トクセイ ニ オヨボス コウサンソ ガンユウ h-BN フンマツ シヨウ ノ コウカ
この論文をさがす
説明
h-BN/feldspar composite was sintered under normal pressure at low temperature in air. Using oxygen-enriched h-BN powder was effective to increase the strength of composites. h-BN powder included 40mass% B2O3, and feldspar which melting point was nearly 1500 K, were mixed at a volume ratio of 1:1. The mixed powder was sintered without pressure at 1573 K in air. The average bending strength of the compacts was 47 MPa. It was revealed that the existence of melted B2O3 during sintering was the key point for both getting good wettability of the interface between h-BN and feldspar, and getting high strength of the composites.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 58 (12), 733-737, 2011
一般社団法人 粉体粉末冶金協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681288348928
-
- NII論文ID
- 10030479643
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BC38Xht1ansg%3D%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 023403454
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可