- Fabrication of Super-Elastic Ti-10V-2Fe-3Al Alloy Compacts by MIM Process
- MIMプロセスによる超弾性Ti-10V-2Fe-3Al合金の創製
- MIM プロセス ニ ヨル チョウダンセイ Ti 10V 2Fe 3Al ゴウキン ノ ソウセイ
この論文をさがす
抄録
Titanium alloys have been used especially as aerospace, medical and dental materials because of their excellent attributes of high corrosion resistance and high specific strength. A Ti-10V-2Fe-3Al is one of β-titanium alloy and it shows super-elasticity. In this study, the fabrication of super-elastic Ti-10V-2Fe-3Al alloy compacts by metal injection molding which is one of near net shape forming of powders was investigated using mixed elemental and alloy powders. Under the optimized MIM process condition, nearly full density (97∼98 %) was obtained and the tensile properties of strength and elongation were 1000∼1050 MPa and around 5 %, respectively. Moreover, after solution treatment and aging, the compacts with alloy powder showed clearly super-elasticity.
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 58 (6), 361-366, 2011
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681288742784
-
- NII論文ID
- 10029437779
-
- NII書誌ID
- AN00222724
-
- COI
- 1:CAS:528:DC%2BC3MXos1elurc%3D
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 11158450
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可