Microstructures and textures of 1050 aluminum produced by equal channel angular pressing.
-
- CUI Qi
- Technical Development Center, Mitsubishi Aluminum Co., Ltd.
-
- OHORI Koichi
- Technical Development Center, Mitsubishi Aluminum Co., Ltd.
Bibliographic Information
- Other Title
-
- ECAP加工を施した1050アルミニウムの組織と集合組織
- ECAP カコウ オ ホドコシタ 1050 アルミニウム ノ ソシキ ト シュウゴウ ソシキ
Search this article
Abstract
The evolution of microstructure and texture of 1050 aluminum sheets was investigated by the method of equal channel angular pressing (ECAP). Repetitive pressings were used on the same samples, up to a total of 8 pressings through the die, with the samples pressed following two different processing routes either without rotation (route A) or with rotation through 180° (route B). The result shows that the high angle grain boundaries increase, and the grain sizes are reduced with repetitive pressings. The rate of formation of the high angle grain boundaries depends upon the processing routes and is more rapid using route A than using route B. Moreover, the shear texture, composed of {001}<110> and {111}<110> components, was observed after 1 pressing. However, the texture, {001}<010> component specially, is reduced with the repetitive pressings. Such a change of texture does not depend upon the processing routes nearly. By subsequent annealing, the intensity of the {111}<110> component is not almost changed, but that of {001}<110> component decreases largely and no new texture component appears.
Journal
-
- Journal of Japan Institute of Light Metals
-
Journal of Japan Institute of Light Metals 49 (4), 155-160, 1999
The Japan Institute of Light Metals
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681311776512
-
- NII Article ID
- 10002666265
- 10010395108
-
- NII Book ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK1MXivVWjt7c%3D
-
- ISSN
- 18808018
- 04515994
-
- NDL BIB ID
- 4705311
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed