アルミナ粒子分散型Al‐Cu‐Mg系複合材料の時効析出

書誌事項

タイトル別名
  • Aging behaviour of Al2O3-particle-dispersed Al-Cu-Mg alloy composite materials.
  • アルミナ リュウシ ブンサンガタ Al Cu Mgケイ フクゴウ ザイリョウ

この論文をさがす

抄録

Aging behaviour of Al2O3-particle-dispersed (20vol%) Al-3.96%Cu and Al-4.09%Cu-1.58%Mg alloy composite materials was investigated by means of microvickers hardness, electrical resistivity measurements and transmission electron microscopy. In a case of an Al2O3/Al-3.96%Cu composite materials θ' phase precipitates on subgrain boundaries at an early stage of aging at 423K. After a prolonged agings an increased number of θ' precipitates are seen inside grains. While GP zones form normally in an Al-3.96%Cu alloy at this aging condition, no GP zones precipitate in the Al2O3/Al-3.96%Cu composite material and age-hardening does not take place. On the contrary, age-hardening is clearly observed in an Al2O3/Al-4.09%Cu-1.58%Mg composite material aged at 423K. In this composite material, both GP zones and θ' precipitates are found inside grains, being different from GPB zones and S' intermediate phases normally formed in an Al-4.09%Cu-1.58%Mg alloy.

収録刊行物

  • 軽金属

    軽金属 41 (11), 752-758, 1991

    一般社団法人 軽金属学会

被引用文献 (16)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ