Ａｌ‐Ｌｉ系合金のじん性と層状割れ

DOI Web Site 被引用文献5件

書誌事項

タイトル別名
  • Toughness and laminated cracks in Al-Li system alloys.
  • Al Liケイ ゴウキン ノ ジンセイ ト ソウジョウ ワレ

この論文をさがす

説明

In this study, the relationships between toughness and laminated cracks were investigated on 8090 Al-Li system alloys. In 8090V notched specimens, total absorbed energy increases with decreasing temperature up to 142K, and then decreases at 77K. This phenomenon is closely associated with the change in the number of laminated cracks on the fracture surface. Absorbed energy for forming laminated cracks is greatest at 142K. Crack propagation energy, then, increases, which results in increasing total absorbed energy. Dynamic fracture toughness and the number of laminated cracks increase with decreasing temperature. The maximum dynamic fracture toughness value is obtained at 5K. Dynamic fracture toughness increases due to the increase in the number of laminated cracks. Modified microcrack toughening concept is introduced for explaining increasing toughness by laminated cracks. The calculating value of increasing ratio in fracture toughness between R. T. and 77K is in good agreement with the experimental value of increasing ratio in fracture toughness. This result suggests that the effect of stress release by laminated cracks near the crack tip is the main cause for increasing toughness of Al-Li system alloys at low temperature.

収録刊行物

  • 軽金属

    軽金属 43 (2), 95-101, 1993

    一般社団法人 軽金属学会

被引用文献 (5)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ