- Production of Al-12mass%Si alloy rapidly solidified clad strip by melt drag process.
- メルトドラッグホウ ニヨル Al 12 massパーセント Si ゴウキン キ
この論文をさがす
抄録
This study was attempted to produce rapidly solidified clad strip by a melt drag process and to examine the clad strip properties. Roll speed V and cooling length L were chosen as principal producing factors. Clad strips consisting of base and overlay strips rigidly bonded with clear bonding interface are produced under the condition where roll speed V was varied from 30 to 70m/min and cooling length L was varied from 25 to 100mm. Clad strips of base and overlay strip both rapidly solidified are produced by cooling length between 75 and 100mm with a constant rolling velocity 50m/min.
収録刊行物
-
- 軽金属
-
軽金属 45 (12), 685-690, 1995
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681313150080
-
- NII論文ID
- 10001725909
- 10004013247
-
- NII書誌ID
- AN00069773
-
- COI
- 1:CAS:528:DyaK28XltVSruw%3D%3D
-
- ISSN
- 18808018
- 04515994
- http://id.crossref.org/issn/04515994
-
- NDL書誌ID
- 3641891
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可