高圧凝固法によるルチル型ＴｉＯ２粉末／アルミニウム複合材料の製造と組織的特性

DOI Web Site 被引用文献9件

書誌事項

タイトル別名
  • Fabrication of particulate rutile TiO2/Al composites by squeeze casting and their structural characteristics.
  • コウアツ ギョウコホウ ニ ヨル ルチルガタ TiO2 フンマツ アルミニウム

この論文をさがす

抄録

Rutile TiO2/Al composites were prepared by squeeze casting method and the reactivity between the reinforcement and the matrix was investigated. Three kinds of composite structures were found depending on the fabrication temperatures. The first one was the non-reacted composites of TiO2/Al, the second one was the reacted homogeneous composites and the last one was the reacted heterogeneous composites composed of complex multiple phases. The hardness of the reacted homogeneous composites was about HV1100, while the hardness of the reacted heterogeneous composites ranged from HV40 to 1250. X-ray diffraction pattern and SEM analysis showed that, the hardened reacted homogeneous composites was composed of fine α-Al2O3 dispersed in the Al-Ti intermetallic compound matrix.

収録刊行物

  • 軽金属

    軽金属 43 (1), 26-32, 1993

    一般社団法人 軽金属学会

被引用文献 (9)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ