グルコン酸や亜鉛イオンを含む模擬海水におけるA3003アルミニウム合金の腐食による形態変化とその機構
書誌事項
- タイトル別名
-
- Corrosion-induced morphological changes and the mechanism of A3003 aluminum alloy in model sea water containing gluconates and zinc ions
- グルコンサン ヤ アエン イオン オ フクム モギ カイスイ ニ オケル A3003 アルミニウム ゴウキン ノ フショク ニ ヨル ケイタイ ヘンカ ト ソノ キコウ
この論文をさがす
説明
<p>Corrosion mechanism and morphology changes of aluminum alloy in model solution corresponding sea water containing gluconates and zinc ions were investigated by immersion corrosion tests with surface analysis. Surface and cross-sectional SEM results showed that zinc ions suppress the morphology changes of aluminum alloy in the solution containing gluconates. XPS analyses indicated that gluconates in the solutions adsorb on the oxide films of aluminum alloy and protective films of the adsorbed gluconates would prevent the penetration of chloride ions to the aluminum alloy. The XPS results also suggest that zinc ions in the solutions bond to the oxide film of aluminum alloy and zinc ions enhance the corrosion inhibition ability of the protective films of gluconates for aluminum alloy in model sea water.</p>
収録刊行物
-
- 軽金属
-
軽金属 68 (1), 16-21, 2018
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681315235072
-
- NII論文ID
- 130006405253
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- HANDLE
- 2115/75933
-
- NDL書誌ID
- 028775720
-
- 本文言語コード
- ja
-
- 資料種別
- journal article
-
- データソース種別
-
- JaLC
- IRDB
- NDLサーチ
- Crossref
- CiNii Articles
- KAKEN
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可