工業用純アルミニウム／タフピッチ銅摩擦圧接継手の引張強さおよび疲れ強さの変形入熱による評価

DOI DOI Web Site Web Site Web Site 被引用文献1件 参考文献18件 オープンアクセス

書誌事項

タイトル別名
  • Evaluation of Tensile Strength and Fatigue Strength of Commercial Pure Aluminum/Tough Pitch Copper Friction-Welded Joints by Deformation Heat Input
  • コウギョウヨウ ジュン アルミニウム タフ ピッチ ドウ マサツ アッセツ ツギテ ノ ヒッパリ ツヨサ オヨビ ツカレ ツヨサ ノ ヘンケイ ニュウネツ ニ ヨル ヒョウカ

この論文をさがす

説明

The relationship between joint strength and deformation heat input at the upset stage and the relationship between joint strength and upset burn-off length were examined on friction welded joints of 1050 pure aluminum to C1100 tough pitch copper. Joint quality was evaluated from the tensile strength and fatigue strength. It was found that both the deformation heat input at the upset stage and the upset burn-off length correlated well with joint strength. Additionally, when the deformation heat input at the upset stage or upset burn-off length exceeded a certain value, stable tensile strength was obtained. The mixing layer, intermetallic compounds of Al-Cu were interpolated into A1050, formed at the weld interface, and joints having a thick mixing layer fractured at the weld interface. Joint efficiencies of sound joints for the fatigue limit of the A1050 base metal were 88–100%. Judging from the fatigue limit, sound joints could be produced when either the deformation heat input at the upset stage or the upset burn-off length exceeded a certain value.

収録刊行物

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 49 (12), 2786-2791, 2008

    公益社団法人 日本金属学会

被引用文献 (1)*注記

もっと見る

参考文献 (18)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ