- The temperature dependence of mechanical properties in Al-Cu single crystals
- Al Cu ゴウキン タンケッショウ ニ オケル キカイテキ セイシツ ノ ヘ
この論文をさがす
抄録
Al-0.5, 1.0 and 1.5 at% Cu alloy single crystals were quenched from 500°C. All the alloys allow a similar stress-strain behavior. The stress-strain curves show serrations near room temperature and yielding phenomena above 300°C. CRSS reversely depends on temperatures from -78° to 80°C. A peculiar maximum in CRSS is found at 80°C. When the strain rate in this region changes from ε1 to ε2 (ε1 > ε2), difference in the flow stress decreases resulting inτ2 > τ1 at room temperature. Edge dislocations forming dipoles uniformly distribute at -196°C, and tend to cluster at elevated temperatures. Long dislocation loops are found at 100°C, which are formed by the intersection with prismatic dislocation loops grown during heating. A peak in CRSS at 80°C and a stress exponent above 300°C are also theoretically described.
収録刊行物
-
- 軽金属
-
軽金属 27 (12), 584-589, 1977
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681315507968
-
- NII論文ID
- 130004207910
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 1917812
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可