- Effect of solution treatment condition on the hot workability of 5083 Al alloy
- 5083 ゴウキン ノ ネッカン カコウセイ ニ オヨボス カコウ マエ キン
この論文をさがす
抄録
Hot torsion tests were conducted on the 5083 aluminum alloy having cast structure under the conditions of shear strain rate range from 0.1 to 75 sec-1 and temperature range from 400°C to 500°C. The two stages solution treated materials are superior in hot workability than one stage treated ones. It is possible by electron microprobe analyses to deduce the composition and relative amount of constituent elements of the precipitated intermetallic compounds which decrease the ductility of the alloy. These intermetallic compounds are composed of such elements as Fe, Mn, Cr and Si.
収録刊行物
-
- 軽金属
-
軽金属 27 (12), 579-583, 1977
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681315510016
-
- NII論文ID
- 130004207909
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 1917815
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可