Self-healing corrosion protective capability of polymer coatings for aluminum
-
- Yabuki Akihiro
- Division of Chemical Engineering, Faculty of Engineering, Hiroshima University
-
- Okuno Hironao
- Graduate Student, Graduate School of Engineering, Hiroshima University
Bibliographic Information
- Other Title
-
- アルミニウムにおけるポリマコーティングの自己修復性防食作用
- アルミニウム ニ オケル ポリマコーティング ノ ジコ シュウフクセイ ボウショク サヨウ
Search this article
Abstract
The self-healing corrosion protective properties of polymer coatings for aluminum were investigated. Zirconium phosphate conversion coating and polymer coating, which are various primer and top coatings with a thickness of 5 and 11 μm, were applied to the surface of pure aluminum, and after creating a defect by means of a knife-edge, a corrosion test was carried out in 0.5 mass% NaCl solution at 40°C. The polarization resistance of each coating was measured using electrochemical impedance method to evaluate the self-healing capability of coatings. The polarization resistance of scratched specimen coated polymer containing pigment increased with increasing time, resulting in high resistance. Thus, the self-healing capability of the polymer coating was recognized. The healing film formed on the scratched surface contained carbon. Analyzing component eluted from the coating, diethyl phthalate was detected. Polarization measurement of aluminum substrate in corrosive solution with the organic compound was conducted, and it was confirmed that the organic compound has the inhibiting effect against corrosion. The results showed that the organic compound was related to the formation of healing film.
Journal
-
- Journal of Japan Institute of Light Metals
-
Journal of Japan Institute of Light Metals 61 (12), 724-728, 2011
The Japan Institute of Light Metals
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681315841152
-
- NII Article ID
- 10030515012
-
- NII Book ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL BIB ID
- 023359814
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed