- Embrittlement of 5083 alloy by liquid gallium.
- 5083 ゴウキン ノ エキタイ ガリウム ニ ヨル ゼイカ
この論文をさがす
抄録
The effect of grain boundary precipitates on the embrittlement of 5083 alloy solutionized, aged at 150°C for various periods and coated with liquid Ga was investigated by means of tensile test and microscopy. Ga coated 5083 alloy fractures along grain boundaries. The shorter the aging time, the lower the fracture stress of Ga coated alloy, though ultimate tensile strength of the alloy uncoated. is independent of the aging time. When the alloy was held at 35°C for various periods after Ga coating, the fracture stress becomes to be zero after a critical holding period tf. A relation between fracture stress σf and holding time t is expressed as σf=σf0-k•t1/2, where σf0 and k are constants.
収録刊行物
-
- 軽金属
-
軽金属 35 (10), 568-573, 1985
一般社団法人 軽金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681316242432
-
- NII論文ID
- 130004208506
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 3058422
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可