Abnormal grain growth in 5056 alloy plates
-
- SHIMIZU Kyoji
- Faculty of Engineering, Univ. of Osaka Pref.
-
- NAKATANI Yoshizo
- Faculty of Engineering, Univ. of Osaka Pref.
-
- SATO Masuhiro
- Faculty of Engineering, Univ. of Osaka Pref.
-
- SAKAMOTO Hiroshi
- Teikoku Sangyo Co., Ltd.
-
- HARADA Hiroshi
- Toyo Aluminium, Co., Ltd.
-
- HINODA Yuji
- Fuji Sash Kogyo Co., Ltd.
Bibliographic Information
- Other Title
-
- 5056合金の異常粗粒化現象
- Secondary recrystallization of aluminum alloys (1st report)
- アルミニウム合金の2次再結晶(第1報)
Abstract
Abnormal grain growth was observed in 5056 alloy.<br>Metallographic examinations were made for the following two series of alloys.<br>Series A: Al-Mg binary system, hot and cold rolled.<br>Series B: Al-5%Mg alloys containing small amounts of Mn and/or Cr, hot and cold rolled.<br>The results obtained were as follows.<br>(1) The abnormal grain growth in 5056 alloy was closely related with Cr and/or Mn contents. The phenomenon took place at under 0.3%Cr contents and/or 0.4% of Mn contents.<br>(2) The secondary recrystallization temperature was higher and the ultimate maximum grain size was smaller with the increase in Mn and/or Cr contents.<br>(3) The abnormal coarse grains in the outer layer of the plate were discoidal; while, the grains in the middle layer remained fine.
Journal
-
- Journal of Japan Institute of Light Metals
-
Journal of Japan Institute of Light Metals 19 (6), 233-240, 1969
The Japan Institute of Light Metals
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681316325888
-
- NII Article ID
- 130004207097
-
- ISSN
- 18808018
- 04515994
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed