- Texture and bending workability of commercial-purity aluminum and Al–Mg alloy sheets subjected to laser irradiation
- レーザ ショウシャ オ ホドコシタ コウギョウヨウ ジュンアルミニウム オヨビ Al-Mg ゴウキンバン ノ シュウゴウ ソシキ ト マゲ カコウセイ
この論文をさがす
説明
The study of texture control in aluminum alloys is thriving. For example, Cube orientation has been found to be effective for improving bending workability of Al–Mg–Si alloys. In this study, commercial-purity aluminum (A1050-H18) and Al–Mg alloy (A5052-O) plates were irradiated by a laser beam, measured using a SEM apparatus and then bending tested. In A1050-H18 subjected to slower laser irradiation, Cube orientation was developed as a result of recrystallization due to the higher achieving temperatures than 680 K. In A5052-O, on the other hand, Cube orientation was developed in all the investigated irradiation conditions. From IPF maps of both of specimens, preferential orientation was found to be accumulated into the ‹001› direction, resulting in the softening and thus enhanced bending workability by the laser irradiation, while ‹101› direction containing Goss orientation is reduced. The area fraction of Cube orientation did not affect the bending workability, suggesting that softening has a synergistic effect with texture control.
収録刊行物
-
- 軽金属
-
軽金属 65 (8), 339-343, 2015
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681316727424
-
- NII論文ID
- 130005100684
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 026686648
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可