Environmental embrittlement of Al-Mg-Si alloys in air
-
- ANDOH Makoto
- Tokyo University
-
- ASAKURA Kentaroh
- Faculty of Engineering, Tokyo University
-
- KANNO Motohiro
- Faculty of Engineering, Tokyo University
Bibliographic Information
- Other Title
-
- Al‐Mg‐Si系合金の大気環境脆化
Abstract
Environmental embrittlement was studied by use of round tensile specimens of two kinds of alloys: Al-1.12 mass%Mg2Si-0.35Si (S-alloy) and Al-1.47%Mg2Si-0.34%Cu (BC-alloy). They were solution treated at 540°C for 1 h, quenched in water and aged at 175°C for indicated times: 30 min (under aging), 103 min (peak aging), and 104 min (over aging). After heat treating, they were tested at an initial strain rate of 1.7×10-4/s or 1.7×10-7/s in a laboratory air with relative humidity of about 100%. When tested at the strain rate of 1.7×10-7/s, the peak aged S-alloy showed embrittlement with lower tensile elongation and reduction in area compared with a strain rate of 1.7×10-4/s. The embrittlement also appeared on the other aging conditions (under aging, over aging), and it was most apparent on over-aged alloy despite their lower tensile strength. By means of EDS analysis, Si-rich precipitates were detected on intergranular fracture surface of over-aged alloy. In contrasted to foregoing experimental results on S alloy, no embrittlement appeared in the BC-alloy irrespective of aging condition. Thus, the embrittlement is thought to be stimulated by the Si-rich precipitates which are increased with the progress of aging.
Journal
-
- Journal of Japan Institute of Light Metals
-
Journal of Japan Institute of Light Metals 55 (10), 468-472, 2005
The Japan Institute of Light Metals
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282681317616256
-
- NII Article ID
- 130004481704
-
- COI
- 1:CAS:528:DC%2BD2MXhtlWht7nE
-
- ISSN
- 18808018
- 04515994
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed