Ti–Al系合金マイクロチャンネル内壁のマルチスケールポーラス構造に及ぼす陽極酸化時間の影響

DOI HANDLE Web Site Web Site 参考文献16件 オープンアクセス

書誌事項

タイトル別名
  • Effect of anodizing time on multiscale porous structure of Ti–Al alloy microchannel wall
  • Ti-Alケイ ゴウキン マイクロチャンネル ナイヘキ ノ マルチスケールポーラス コウゾウ ニ オヨボス ヨウキョク サンカ ジカン ノ エイキョウ

この論文をさがす

抄録

<p>Effect of anodizing time on the multiscale porous structure of the inner wall of the microchannel produced in a titanium alloy body has been investigated. The microchannel was produced by a powder-metallurgical process in which a titanium-powder compact containing thin aluminum wire was sintered at a temperature above the melting point of aluminum. During sintering, microscopic infiltration of molten aluminum into the porosity of the compacted titanium powder and subsequent diffusion of aluminum into the titanium powder particles brought about the formation of a microchannel lined with Ti–Al alloy layer in the sintered body. The inner walls of the microchannels with uniform composition, Ti–18.0(±1.8)mol%Al, were provided for anodizing experiments. When the anodizing time was in the range from 1.8 to 28.8 ks, the structure of the anodic oxide film was nanotube array. Each specimen had a microchannel of several hundred micrometers in diameter, inner wall asperity of several ten micrometers in size, and nanotube array structure of the anodic oxide film. In the specimen anodized for 59.6 ks, on the other hand, the nanotube array had changed to a different structure resembling that of nanoporous metals produced by dealloying.</p>

収録刊行物

  • 軽金属

    軽金属 67 (11), 589-594, 2017

    一般社団法人 軽金属学会

参考文献 (16)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ