- Filling velocities and defects of plate shaped diecastings.
- ウスニク ヘイバンジョウ ダイカスト イモノ ノ ジュウテン ソクド ト チュ
この論文をさがす
抄録
The casting defects are reduced by increasing the molten metal velocity near the defects. When the linear runner, where flowout volume through the lower runner gate was greater than the volume through the upper one, was used, the molten metal unequally filled up the cavity and the molten metal velocity suddenly decreased at a final filling portion. Therefore, the casting defects frequently occurred at the final filling portion. On the other hand, when the stair shaped runner was used, the molten metal equally filled up the cavity without a turbulent flow, and the molten metal velocity did not decrease at the final filling portion. Therefore, the molten metal filled up the cavity with inconsiderable casting defects in a short time.
収録刊行物
-
- 軽金属
-
軽金属 37 (1), 48-52, 1987
一般社団法人 軽金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681317785600
-
- NII論文ID
- 130004075745
- 10008560886
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 3120525
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可