CO<sub>2</sub>ガス冷却原子炉用燃料被覆材マグノツクス合金の改良についての二三の実験
書誌事項
- タイトル別名
-
- Some experiments on the improvement of Magnox alloys used for canning material in CO<sub>2</sub> gas-cooled reactor
抄録
As the first step to improve Magnox series alloys currently used in Calder Hall power reactor in England as well as to develop better magnesium alloys to be used for canning materials in CO2 gas-colled reactor, the following experiments have been carried out:<br>By preparing, in the authors own laboratory Magnox E alloy, as well as several Mg-Al-Ca-Be alloys of different amount of calcium and berylium, but less than those in Magnox E, the effect of the two elements on the properties of the alloys have been confirmed. The two elements improved strength and oxidation resistance; calcium being more effective in strengthening as seen in Fig. 1.<br>Substitution of calcium with other element of lower thermal neutron absorption cross section (less than 1 barn) was the subject of next concern, as calcium is not recommended because of welding crack problem. Work hardening characteristic and annealing curves shown in Fig. 2 and 3, respectively have been compared and little differences has been found in the former among the candidate alloys without calcium. Considering from the annealing curves, the high temperature strength at the working temperature of reactor, 752°F (400°C), may be improved by the addition of zirconium, zinc or bismuth, about which further experiments are being contemplated.
収録刊行物
-
- 軽金属
-
軽金属 7 (6), 68-72, 1957
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681317789696
-
- NII論文ID
- 130004209574
-
- ISSN
- 18808018
- 04515994
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可