工具鋼　マルエージング鋼のヒートチェック性におよぼすＮｉ量の影響

DOI Web Site

書誌事項

タイトル別名
  • Tool Steels. Influence of Ni Content on the Property of Heat Checking in Maraging Steel.
  • マルエージング鋼のヒートチェック性に及ぼすNi量の影響
  • マルエージング コウ ノ ヒート チェックセイ ニ オヨボス Niリョウ ノ

この論文をさがす

説明

Effect of Ni content, range of 6% to 24%, on the heat checking resistance of 4%Mo -8%Co maraging steel were studied. The experimental results are as follows. (1) The heat-checking resistance for the total number, mean length and maximum length of heat checks, were improved with decreasing Ni content. In order to improve heat-checking resistance quantitatively, Ni content must be lowering to 18% at 873K, 12% at 923 and 973K, respectively. But crack length was significant level at 973K heat-checking test. (2) The effect of Ni was quantitatively converted to the HC value. HC= (Heat checking temp.) / (As temp.) Heat checking temp.:Heat checking temperature (K) As temp.:Austenite transformation temperature gained by 150K/s heating rate(K) ,which is equal to heat checking test . The heat-checking resistance were decreased drastically the HC value, above 1.0, whereas improved gradually with decreasing the HC value, below 1.0. (3) Austenite retransformation has occurred the HC value, above 1.0

収録刊行物

  • 電気製鋼

    電気製鋼 68 (2), 87-94, 1997

    大同特殊鋼株式会社

詳細情報 詳細情報について

問題の指摘

ページトップへ