水素化チタンの熱分解反応を利用した純チタン粉末材の創製

DOI Web Site 被引用文献2件 参考文献17件

書誌事項

タイトル別名
  • Fabrication of Powder Metallurgy Pure Ti Material by Using Thermal Decomposition of TiH<SUB>2</SUB>
  • スイソカ チタン ノ ネツ ブンカイ ハンノウ オ リヨウ シタ ジュンチタン フンマツザイ ノ ソウセイ
  • Fabrication of Powder Metallurgy Pure Ti Material by Using Thermal Decomposition of TiH2

この論文をさがす

説明

  Titanium (Ti) and titanium alloys have been interested as an engineering material because they are widely used across various industrial applications, for example, motorcycle, automotive and aerospace industries, due to their light weight, high specific strength and superior corrosion resistance. Ti materials are particularly significant for the aircraft using carbon/carbon (C/C) composites, for example, carbon fiber reinforced plastics (CFRP), because Ti materials are free from the problem of contact corrosion between C/C composites. However, the applications of Ti materials are limited because of their high cost. From a viewpoint of cost reduction, cost effective process to fabricate Ti materials is strongly required. In the present study, the direct consolidation of titanium hydride (TiH2) raw powders in solid-state was employed to fabricate pure Ti bulk materials by using thermal decomposition of TiH2. In general, the production cost of Ti components is expensive due to using commercially pure (CP) Ti powders after dehydrogenation. On the other hand, the novel process using TiH2 powders as starting materials is a promising low cost approach for powder metallurgy (P/M) Ti products. Furthermore, this new process is also attractive from a viewpoint of energy saving because the dehydrogenation is integrated into the sintering process. In this study, TiH2 raw powders were directly consolidated by conventional press technique at 600 MPa to prepare TiH2 powder compacted billets. To thermally decompose TiH2 and obtain sintered pure Ti billets, the TiH2 powder billets were heated in the integrated sintering process including dehydrogenation. The hot-extruded pure Ti material, which was heat treated at 1273 K for 180 min in argon gas atmosphere, showed tensile strength of 701.8 MPa and elongation of 27.1%. These tensile properties satisfied the requirements for JIS Ti Grade 4. The relationship between microstructures, mechanical properties response and heat treatment temperature is discussed in detail.

収録刊行物

  • 高温学会誌

    高温学会誌 37 (6), 326-331, 2011

    一般社団法人 スマートプロセス学会 （旧高温学会）