Effect of Projectile Diameter on Weldability of Impact Welding

DOI Web Site 17 References
  • DATE Hidefumi
    Department of Mechanical Engineering and Intelligent Systems, Faculty of Engineering, Tohoku Gakuin University

Bibliographic Information

Other Title
  • 衝撃圧接の接合性に及ぼすプロジェクタイル径の影響
  • ショウゲキ アッセツ ノ セツゴウセイ ニ オヨボス プロジェクタイルケイ ノ エイキョウ

Search this article

Description

The impact welding has been carried out using the projectile with the diameter of 11 and 5 mm. The large projectile with the slenderness ratio L/d (L is Length and d is diameter) of 1 to 5 was welded to the stainless steel target. However, only the small projectile with the slenderness ratio less than 1.2 was welded to the same stainless steel target. In order to clarify the effect of the diameter of the projectile on the weldability, the temperature elevating process in the cylindrical projectile subjected to a longitudinal impact is evaluated numerically using LS-DYNA. The slenderness ratios used in the analysis were 1.0, 2.0 and 3.0. The coefficient of friction used in the analysis was 0.2. The constitutive equation used in the analysis was Cowper-Symonds type. Those numerical results indicated that the deformation mechanism of the projectile with the slenderness ratio less than 2.0 is different of that of the projectile with the slenderness ratio more than 2.0. It was clarified from those results that the temperature of the small projectile with the slenderness ratio less than 1.5 arrives at the bonding temperature by the difference of the deformation mechanism regardless of the small kinetic energy.

Journal

References(17)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top