Fatigue, Cyclic Deformation and Microstructure. Distribution of Internal Crack Initiation Sites in High-cycle Fatigue for Titanium Alloys.

DOI 機関リポジトリ 機関リポジトリ (HANDLE) HANDLE Web Site 被引用文献3件 参考文献22件 オープンアクセス

この論文をさがす

説明

In order to clarify how the internal crack initiation site distributes according to microstructure in high-cycle fatigue, α-β or near α titanium alloys with various microstructure were subjected to fatigue test in liquid nitrogen. The internal crack initiation occurred longer than 105 cycles at 77 K. The initiation site was a facet or its aggregate which originated from α grain transgranular cracking in each material. In equiaxed α structures, the location of initiation site was obviously restricted to near the specimen surface (i.e. 10-200 μm deep from the specimen surface). In acicular α structures, the location was more or less near the specimen surface and more interior cases were also seen, which were associated with a larger initiation site size. In elongated α structure, on the contrary, the location was scattered from the vicinity of specimen surface to the center in fracture surface. The size of the internal crack initiation sites was evaluated, and the location of the sites was discussed from the viewpoints of the cyclic stress and their size.

収録刊行物

被引用文献 (3)*注記

もっと見る

参考文献 (22)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ