- 早川 泰弘
- 静岡大学電子工学研究所
-
- ARIVANANDHAN Mukannan
- 静岡大学電子工学研究所
-
- 岡野 泰則
- 大阪大学大学院基礎工学研究科
-
- 小澤 哲夫
- 静岡理工科大学理工学部
-
- 稲富 裕光
- 宇宙航空研究開発機構宇宙科学研究所
書誌事項
- タイトル別名
-
- Growth of InGaSb Alloy Semiconductor Bulk Crystals under Microgravity
- ビショウ ジュウリョク カンキョウ カ ニ オケル コンショウハンドウタイ バルク ケッショウ セイチョウ
この論文をさがす
説明
The review reported the microgravity experiments performed using space shuttle, drop tower and Chinese recovery satellite. In addition, the experimental plan for microgravity experiment in the International space station was introduced. From the space shuttle experiment, it was found that the space-grown sample with free melt surface was almost spherical and Marangoni convection enhanced the melt mixing. Whereas the melt mixing without free melt surface was controlled by diffusion. Formation of spherical projections on the surface of InGaSb was in-situ observed using a high speed CCD camera in the drop experiment. Microgravity studies on the dissolution and crystallization of InxGa1-xSb was carried out having the sandwich combination of GaSb(111)A/InSb/GaSb(111)B using the Chinese recoverable satellite. It was demonstrated clearly that the shape of the solid/liquid interface and composition profiles in the solution was significantly affected by gravity.
収録刊行物
-
- 表面科学
-
表面科学 33 (12), 687-693, 2012
公益社団法人 日本表面科学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681433720832
-
- NII論文ID
- 10031136976
-
- NII書誌ID
- AN00334149
-
- COI
- 1:CAS:528:DC%2BC3sXksFKks78%3D
-
- ISSN
- 18814743
- 03885321
-
- NDL書誌ID
- 024154457
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可