- Microstructural Evolution in Cerium Dioxide Irradiated with Heavy Ions at High Temperature
- コウオン イオン ショウシャシタ サンカ セリウム ノ ソシキ ヘンカ
この論文をさがす
抄録
Formation of subdivided grains and coarsened bubbles in uranium dioxides under high burn-up conditions in nuclear power plants deteriorate the performance of nuclear fuels. To clarify its mechanism, heavy ion irradiations in cerium dioxide followed by Raman spectroscopy, X-ray diffractometry and electron microscopy (SEM) were performed. At the early stage of irradiations, increase in the lattice constant and shift in the F2g peak position were observed presumably indicating accumulation of oxygen vacancies. Further irradiation enhanced recombination or clustering of vacancies depending on the irradiation temperature. The behaviors affect the surface morphology of the sample as well. Especially above 1000K, characteristic changes in Raman spectra and surface features were detected, presumably attributable to remarkable diffusion of vacancies. The relation between displacement of F2g position and electronic energy deposition of incident ions was observed, suggesting the role of electronic excitations on the formation of oxygen vacancies in cerium dioxide.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 71 (12), 1084-1088, 2007
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681453778432
-
- NII論文ID
- 10020007635
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9299936
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可