- Preparation of Highly Active Methanol Steam Reforming Catalysts from Glassy Copper-Zirconium Alloys with Small Amount of Noble Metals
- ショウリョウ ノ キキンゾク オ フクム ドウ ジルコニウム キンゾク ガラス オ モチイタ コウカッセイ メタノール スイジョウキ カイシツ ショクバイ ノ チョウセイ
この論文をさがす
抄録
Methanol steam reforming has been carried out over catalysts prepared from glassy alloy containing a small amount of noble metals. When the alloy is treated at a temperature above the crystallization temperature, the reforming activity increases, whereas the original alloy does not have the similar activity. The reforming activity of the treated alloys increases with the decreasing content of noble metals down to 1 at%. The DSC (differential scanning calorimetry) analysis of the original alloy has revealed that the activity is related to the extent of supercooling and endothermic heat observed between the glassy temperature and crystallization temperature. Furthermore, the copper particle size of the treated alloy is related to the range of supercooling. These results indicate that the noble atoms are uniformly dispersed into the glassy Cu-Zr alloy by heating from the glass transition temperature to crystallization temperature. When the Cu-Zr alloy with a small amount of noble metals is oxidized over the crystallization temperature, the alloy changes to fine copper particles supported on zirconium oxide. A highly active reforming catalyst can be prepared from a glassy Cu-Zr alloy containing a small amount of noble metals.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 71 (8), 615-619, 2007
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681454220544
-
- NII論文ID
- 10019518069
- 130004455872
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 8915071
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可