The effects of yttrium addition on high temperature properties of the 4th generation nickel-base superalloy were studied. Nickel-base superalloys, which possess both creep strength and oxidation resistance, are being required to satisfy high efficiency and reliability of jet engines. 4th generation superalloys contain platinum groups metals such as ruthenium. In order to satisfy creep strength and phase stability, however ruthenium worsens oxidation resistance. Yttrium doping was found to increase the oxidation resistance due to the improved adhesive strength of Al2O3 oxide, and the effects of yttrium doping on creep strength are established in this paper.<br> Yttrium-added TMS-138 alloy (TMS-138Y) showed high creep strength of 4th generation superalloys, however the creep strength was slightly worse than the alloy without yttrium in the high-temperature low-stress creep condition. Microstructural observations confirmed the increase of Topologically Close Packed (TCP) phases in TMS-138Y. This was due to the formation of a yttrium-containing compound, Al0.06Ni0.73Co0.04Y0.18 (at.), which made incoherent interfaces that allowed TCP phases to precipitate by heterogeneous nucleation.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 70 (4), 380-383, 2006
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681454439680
-
- NII論文ID
- 130004455704
- 10017413510
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 7942974
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可