純チタンの結晶粒微細化と酸化物分散強化

DOI Web Site Web Site 被引用文献6件 参考文献15件

書誌事項

タイトル別名
  • Grain Refining and Oxide Dispersion Strengthening of Pure Titanium
  • ジュンチタン ノ ケッショウリュウ ビサイカ ト サンカブツ ブンサン キョウカ

この論文をさがす

説明

  Titanium (Ti) alloys are applied to various products used in the aircraft, automotive and motor cycles industries due to their high specific strength. Ti-6Al-4V (Ti64) is one of the most general Ti alloys, and shows superior mechanical properties i.e. density of 4.43 g/cm3 and tensile strength over than 900 MPa. However, its application is limited because of a poor plastic formability and the expensive raw materials.<br>    In this study, Roll-Compaction (RCP) process was applied to fabricate high strength pure titanium composite reinforced with titanium oxides (TiO2) by using cheap sponge Ti powders as input materials. RCP was effective to improve the mechanical responses by the grain refinement and the in-situ formation of TiO2 dispersions of the matrix. RCPed powder was consolidated by using spark plasma sintering (SPS) process to serve a high density compact. Subsequently, hot extrusion process was applied to the sintered billet to prepare a full density rod specimen. The evaluation of their mechanical properties at room temperature showed high tensile strength of 640 MPa and good elongation of 17%.<br>

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 73 (10), 768-772, 2009

    公益社団法人 日本金属学会

被引用文献 (6)*注記

もっと見る

参考文献 (15)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ