Pitting Corrosion Resistance of Anodized Aluminum-Copper Alloy Processed by Severe Plastic Deformation
-
- Son In-Joon
- Department of Materials Process Engineering, Kyushu University
-
- Nakano Hiroaki
- Department of Materials Science & Engineering, Kyushu University
-
- Oue Satoshi
- Department of Materials Science & Engineering, Kyushu University
-
- Kobayashi Shigeo
- Department of Applied Chemistry and Biochemistry, Kyushu Sangyo University
-
- Fukushima Hisaaki
- Department of Materials Science & Engineering, Kyushu University
-
- Horita Zenji
- Department of Materials Science & Engineering, Kyushu University
Bibliographic Information
- Other Title
-
- 強歪加工を施したAl‐Cu合金の陽極酸化膜の耐孔食性
- 強ひずみ加工を施したAI-Cu合金の陽極酸化膜の耐孔食性
- キョウヒズミ カコウ オ ホドコシタ AI Cu ゴウキン ノ ヨウキョク サンカマク ノ タイコウショクセイ
Search this article
Abstract
The effect of equal-channel angular pressing (ECAP) on the pitting corrosion resistance of anodized Al-Cu alloy was investigated by electrochemical techniques in a solution containing 0.2 mol/L of AlCl3 and also by surface analysis. The time required before initiating pitting corrosion of anodized Al-Cu alloy was longer with ECAP than without, indicating improvement in the pitting corrosion resistance by application of ECAP. Second phase precipitates were present in Al-Cu alloy matrix and the size of these precipitates was greatly decreased by application of ECAP. The precipitates composed of Si and Al-Cu-Si-Fe-Mn were not oxidized during anodization, and the anodic oxide film were absent at the boundary between the normal oxide films and these impurity precipitates. The pitting corrosion of anodized Al-Cu alloy occurred preferentially around these precipitates, the improvement of pitting corrosion resistance of anodized Al-Cu alloy by ECAP appears to be attributable to a decrease in the size of precipitates, which act as origins of pitting corrosion.<br>
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 72 (5), 353-359, 2008
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681456691840
-
- NII Article ID
- 10021150317
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 9514338
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- Abstract License Flag
- Disallowed