90°対称傾角粒界を有するアルミニウム双結晶の引張変形と再結晶

書誌事項

タイトル別名
  • Tensile Deformation and Recrystallization in Aluminum Bicrystal Having Symmetric 90.DEG. Tilt Grain Boundary
  • 90ド タイショウケイカク リュウカイ オ ユウスル アルミニウムソウケッショウ ノ ヒッパリ ヘンケイ ト サイケッショウ
  • Tensile Deformation and Recrystallization in Aluminum Bicrystal Having Symmetric 90° Tilt Grain Boundary

この論文をさがす

説明

  An aluminum bicrystal having a symmetric 90° tilt grain boundary was tensile-deformed at room temperature and subsequently annealed. In the component grains of the bicrystal, two slip systems with almost the same Schmid factor were activated on the primary slip plane. The grains were rotated in the opposite directions, which resulted in the decrease in the tilt angle by 20°. Two different types of deformation bands, i.e. band of secondary slip and kink band were formed in the grains. The deformation was not symmetric about the grain boundary. Recrystallization occurred through strain induced boundary migration predominantly from one of the grains towards the other.<br>

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 70 (10), 790-796, 2006

    公益社団法人 日本金属学会

参考文献 (35)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ