- On the Strength of Tungsten-Fiber-Reinforced Aluminum Composites at High Temperatures
- タングステン センイ オ フクム アルミニウム ノ コウオン キョウド ニ ツイテ
この論文をさがす
説明
In the present study, tensile and creep tests were carried out on aluminum composites containing continuous or discontinuous tungsten fiber at high temperatures up to 545°C. The specimens containing continuous tungsten fiber (10 vol% and 20 vol%) showed very large values of tensile strength at 300°C and 500°C, however the specific strengthening effect of the discontinuous-tungsten-fiber-reinforced aluminum composites were considerably smaller than that of the fiber itself.<BR>The minimum creep rate of the composite containing 20 vol% continuous tungsten fiber was estimated at about 10−4∼10−5%/hr under a load of 6.06 kg/mm2 at 350°C, and the minimum creep rate-temperature curves on the discontinuous fiber were determined under a load of 1.43∼3.05 kg/mm2. By these results, for example, the minimum creep rate for the matrix was 6.0×10−2%/hr under a load of 2.00 kg/mm2 at 350°C, however the minimum creep rate for the composite containing 15 vol% discontinuous tungsten fiber (diameter=25 μ) was 1.4×10−3%/hr under the same condition.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 31 (5), 607-610, 1967
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681457533952
-
- NII論文ID
- 130007332180
- 40018256222
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 8371536
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可