書誌事項
- タイトル別名
-
- Mechanisms on the Occurrence of Surface Roughening in the High Purity Ferritic Stainless Steel Having Strong {111}〈112〉 Texture during Deep Drawing
- 強い{111}〈112〉集合組織をもった高純度フィライト系ステンレス鋼の深絞り成形時の肌荒れ発生機構
- ツヨイ{111}〈 112 〉 シュウゴウ ソシキ オ モッタ コウジュンド フィライトケイ ステンレスコウ ノ フカシボリ セイケイジ ノ ハダ アレ ハッセイ キコウ
- Mechanisms on the Occurrence of Surface Roughening in the High Purity Ferritic Stainless Steel Having Strong {111}^|^#x3008;112^|^#x3009; Texture during Deep Drawing
この論文をさがす
抄録
In high purity ferritic stainless steel having strong {111}〈112〉 texture, the occurrence of surface roughening after deep drawing cup test depends on the way of taking blanks. However, the cause has not been clarified. In this study, the mechanism was examined in two ways. In the first method heterogeneous deformation behavior was examined by crystal plasticity (CP) analysis in which an adjacent two grains model was assumed. In the case that showed higher surface roughening, the direction of crystal rotation across the grain boundaries (GB) was almost the same and the dislocation density in the vicinity of the GB was higher than that in the area apart from the GB. In the case that showed lower surface roughening, crystals rotated in inverse direction across the GB and the dislocation density in the vicinity of the GB was lower than that in the area apart from the GB. In the second method the distribution of strain taking into account surface roughening was examined by EBSD. In the specimen with higher surface roughening, the area with high dislocation densities predicted by Kernel Average Misorientation (KAM) value was recognized along the GB and the convex region tended to coincide with the area with high dislocation densities. These results obtained from CP and EBSD analyses imply that the surface roughening depending on the way of taking blanks is associated with the strong {111}〈112〉 texture and is caused by the accumulated dislocation density along the grain boundaries.<br>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 77 (10), 440-447, 2013
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282681457628032
-
- NII論文ID
- 10031201579
-
- NII書誌ID
- AN00187860
-
- COI
- 1:CAS:528:DC%2BC3sXhvFajsL%2FM
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 024946902
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可