γ線照射下における硫酸中の銅の腐食

DOI Web Site Web Site

書誌事項

タイトル別名
  • Corrosion of Copper in Sulfuric Acid Under γ-Irradiation
  • ガンマセン ショウシャ カ ニ オケル リュウサン チュウ ノ ドウ ノ フショク
  • Corrosion of Copper in Sulfuric Acid Under γ-Irradiation

この論文をさがす

抄録

In order to illustrate the corrosion behavior of metals under radiation, we undertook a systematic study of the corrosion of pure metals in mineral acid under γ-irradiation. In this paper we describe the results of the experiments concerning the corrosion of copper in sulfuric acid. Irradiation cells containing sulfuric acid in the desired concentration in which pure copper plate is immersed is irradiated with a Co-60γ-ray source, the specimens is hauled up from the sulfuric acid and weighed to determine the weight loss; if necessary, the surface of the specimens are examined photographycally, or by X-ray or electron diffraction, and the corrosion products are chemically analysed. The test results are compared to with those of reference runs conducted under the same conditions minus irradiation. The results were as follows: (1) Effect of radtiaion is pronounced above the total dose of 107 r. (2) The loss of weight becomes greater with the higher acidity up to 5 N and then decreases, reaching the minimum at 20 N. But in concentrated sulfuric acid, it is remarkable and a dark green corrosion product is precipitated which is assumed to be composed of CuS. (3) The effect of radiation is mainly due to the decomposition of sulfuric acid and not to the influence on the nature of the metal itself. (4) The above results are discussed from the standpoint of the radiolysis of sulfuric acid solution.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 26 (5), 308-314, 1962

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ