含チタン迅速窒化鋼の窒化による硬度分布の改良に関する研究

DOI DOI Web Site Web Site Web Site 被引用文献1件

書誌事項

タイトル別名
  • Ti-Containing Rapid Nitriding Steel (2nd Report)
  • ガン チタン ジンソク チッカ コウ ノ チッカ ニ ヨル コウド ブンプ ノ カイリョウ ニ カンスル ケンキュウ

この論文をさがす

抄録

We reported in the previous report that we obtained hard and thick hardened layers when Cr-Ti steels (Ti=2∼3%) were nitrized. But the hardness gradient at the boundary between the hardened and the unhardened parts was too large. Therefore, we intended to improve this defect. We prepared six samples (C:0.2∼0.4, Cr:0∼2.25, Ti:2.0∼2.6) and measured the hardness distribution and tested the heat resistance. The results obtained were as follows: (1) Primary nitriding was carried out at high temperature to increase the depth of nitrization, and the secondary nitriding at 650°C to obtain good results. By this double nitriding the surface hardness was not raised and a distinct peak of hardness appeared at the border point between the hardened and the unhardened layers. (2) Next, the primary nitriding was operated at 600∼675°C for the purpose of raising the surface hardness, and the secondary nitriding was done at a slightly higher temperature than that of primary nitriding (700∼750°C) lower the hardness gradient. By this method, we obtained high surface hardness (VHN:900), small hardness gradient and good surface conditions. The hardness was not lowered by reheating about at 600∼700°C.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 26 (6), 398-401, 1962

    公益社団法人 日本金属学会

被引用文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ