- Solution and Precipitation of C and N in Al-killed Steels during Isothermal Heat Treatment
- Al キルド ゴクナン コウ ノ コウオン ショリ ニ オケル N , C ノ キョドウ
この論文をさがす
抄録
Three Al-killed deep drawing steel sheets (sol. Al: 0.04, 0.02, 0.003∼6%) were solution-treated (1250°C×1.5′) and kept isothermally between 200°∼900°C. Precipitation of C and N in the specimens were investigated by chemical analysis, and internal friction. It was found that the rate of N precipitation is the fastest at about 770°C, and there is no simple relation between NIF (interstitially solved N determined by internal friction) and N as AlN, and with increasing sol. Al, CIF at equilibrium decreases over 300°C, and NIF decreases especially between 600°∼700°C,
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 26 (7), 437-442, 1962
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681457720320
-
- NII論文ID
- 40018258127
- 130007332411
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153567
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可