- Precipitation of N, C of Al-killed Deep-Drawing Sheets During Rapid Cooling
- Al キルド ゴクナン コウ ノ キュウソク レイキャク デ ノ N , C ノ キョドウ
この論文をさがす
抄録
Four deep drawing sheets containing different quantitie of sol. Al were heat-treated in laboratory in similar condition to that of hot-rolling strip-mill, and N, C precpitations were examined by internal friction and chemical analysis. The results were as follows: (1) The finishing temperature had little effect on precipitation. (2) The higher the sol. Al content and coiling temperature, the larger were the precipitations of N and C. (3) N and C dissolved interstitially less than expected from chemical analysis. (4) N precipitation promotes that of C. With these results, the mechanism of formation of elongated grains was discussed.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 26 (10), 678-684, 1962
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681457826432
-
- NII論文ID
- 130007332521
- 40018258019
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153459
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可