- Anodic Formation of the Higher Oxide Film on Nickel (Significance of the Potential in the Anodic Formation of Oxide Films on Nickel, 2nd Report)
- ニッケルアノード ニ オケル コウキュウ サンカブツ ヒマク ノ セイセイ ニ ツイテ
この論文をさがす
抄録
A theoretical investigation was made on the anodic formation of the higher-valence oxides on nickel from the standpoint of the electrochemical thermodynamics. On the electrode of Ni|compact NiO|H2O polarized with a constant anodic current the potential difference in NiO increases in proportion to the film thickness. This potential difference can be expressed in the form on EII=(Ni⁄NiO)μ\ominus−(NiO⁄H<SUB>2O)</SUB>μ\ominus, and the chemical potential of the dissolved nickel atom in NiO is given by (NiO⁄H<SUB>2O)</SUB>μNi=(Ni)μNi−2FEII at the phase boundary of NiO|H2O. (NiO⁄H<SUB>2O)</SUB>μNi decreases with the increase of EII until it reaches the critical value of (NiO⁄H<SUB>2O)</SUB>μNi≤(Ni)μNi+4Ac, where Ac is the affinity of the disproportionation reaction (c): NiO→\dfrac14Ni3O4+\dfrac14Ni. This reaction can proceed only when (NiO⁄H<SUB>2O)</SUB>μNi becomes less than the critical value shown above. Therefore, beyond the critical electrode potential which is given by E(NiO⁄Ni<SUB>3O4)</SUB>=Ea+4Ac⁄2F, the surface film becomes a double oxide film composed of NiO and Ni3O4.The equilibrium potential of Ni|NiO|Ni3O4|H2O electrode can be given by the equilibrium potential for the redox reaction of (f): 3NiO+H2O→Ni3O4+2H++2e, which is also equal to E(NiO⁄Ni<SUB>3O4)</SUB>. When the potential difference in Ni3O4 exceeds the critical value at which the disproportionation reaction (d): Ni3O4→\dfrac43Ni2O3+\dfrac13Ni occurs, the surface film changes again to a triple oxide film of NiO|Ni3O4|Ni2O3.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 24 (3), 183-187, 1960
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681457875840
-
- NII論文ID
- 40018257650
- 130007332562
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153090
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可