This paper describes the testing results of Cr3C2-TiC-Ni cermet prepared by the infiltration method. The cermet was prepared by mixing and compacting carbide powders and subsequently infiltrating with Ni alloy containing 35%Cr3C2 at 1,280°C for 20 min in vacuum. The best of cermets is TiC(10∼20%)-Cr3C2-Ni alloy, which has a 100-hr transverse rupture strength of 89 kg/mm2 at 850°C, and this value exceeds that of TiC-Ni cermet (67 kg/mm2). In respect of oxidation resistance also, this material is very superior.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 24 (3), 158-162, 1960
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681457890304
-
- NII Article ID
- 130007332578
- 40018257646
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 9153086
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed