Effect of Carbon Contents on Corrosion Resistance and Mechanical Properties of Ni-Mo-Cr Alloys
Bibliographic Information
- Other Title
-
- Ni-Mo-Cr合金の耐食性および機械的性質におよぼすCの影響
- Ni-Mo-Cr ゴウキン ノ タイショクセイ オヨビ キカイテキ セイシツ ニ オヨボス C ノ エイキョウ
Search this article
Abstract
Effect of C contents on the properties of Ni-Mo-Cr alloys has been investigated by hardness, tensile, microscopic tests and corrosion tests, made with specimens in boiling 10 and 2 wt%HCl for 24 hours. The following results have been obtained: (1) With increasing content of carbon, both the corrosion loss and the hardness of solution-treated Ni-Mo-Cr alloys increased, but the elongation was lowered. This may be attributable to an increase of eutectic carbide (M6C a=11.03 Å), the amount of which increased by addition of carbon. (2) After annealing at 700° and 800°C for 30 min, the higher carbon contents, the more appreciably deteriorated the corrosion resistance due to the continious precipitation of carbide on grain boundaries.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 25 (8), 544-548, 1961
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681457961728
-
- NII Article ID
- 130007332685
- 40018257969
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 9153409
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed