- Effect of Zinc and Aluminium on Corrosion of Aluminium Brass by Polluted Water
- アルミニウム オウドウ ノ オセンスイ フショク ニ オヨボス アエン オヨビ アルミニウム ノ エイキョウ
この論文をさがす
抄録
A reason for the widespread use of aluminium brass in heat exchanger tubes may be attributed to its high corrosion and erosion resistance. Aluminium brass, however, suffer from a polluted water corrosion at power station using a polluted sea water. Its corrosion occures with sulpher compounds which are released by the action of bacteria. Therefore, the potentiostatic measurements of polarization curve for aluminium brass including various contents of zinc and aluminium were carried out in slowly stirring 3%NaCl aqueous solution containing 1 p.p.m. cystine.<BR>The results obtained were as follows:<BR>(1) Mainly, cystine accelerates cathodic reaction rate, its effect is remarkable esspecially in absence of oxygen.<BR>(2) Although effects of zinc and aluminium contents on electrochemical properties relate linearly to zinc equivalent, there is a discontinuous point at about 32%Zn eq., below which cathodic critical current decreases with zinc equivalent and anodic current increases with either of decrease of aluminium content or increase of zinc content, but above which these currents increase with zinc equivalent respectively.<BR>(3) There are some relation between these discontinuous points and precipitation of β phase.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 27 (7), 337-341, 1963
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681457988992
-
- NII論文ID
- 130007332741
- 40018258266
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153706
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可