- On the New Elinvar-type Alloy “Moelinvar” in the Ternary System of Cobalt, Iron and Molybdenum
- Co-Fe-Moケイ シン コウ ダンセイ ゴウキン モエリンバー ニ ツイテ
- On the New Elinvar-type Alloy “Moelinvar” in the Ternary System of Cobalt, Iron and Molybdenum
この論文をさがす
抄録
Thermal expansion coefficient, rigidity modulus and its temperature coefficient were measured for the alloys containing 45 to 80 per cent of cobalt, less than 25 per cent of molybdenum and the rest of iron. The least coefficient of linear expansion in the temperature range 20° to 50° was 5.70×10−6 which was found in an alloy containing 55 per cent of cobalt and 12.5 per cent of molybdenum. The temperature coefficient of rigidity modulus in the same temperature range was generally negative. However, as the compositions approached the ones, at which the thermal expansion coefficient showed its least value, the absolute value of the coefficient diminished, became zero, changed its sign; and reached a positive maximum value (+14.6×10−5) at compositions corresponding to the ones for the least expansion coefficient. Thus, it will be shown that there are certain composition ranges in this system in which the alloys show elinvar-type properties, and those alloys were named “Moelinvar”. Further, the rigidity modulus at 20° was also determined to get the results that the modulus showed a maximum value (9.89×105 kg/cm2) at the composition containing 45 per cent of cobalt and 15 per cent of molybdenum, and a minimum value (6.08×105 kg/cm2) at the composition of 65 per cent of cobalt and 10 per cent of molybdenum.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 24 (1), 44-46, 1960
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458166912
-
- NII論文ID
- 130007332883
- 40018257523
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9152963
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可