- Magnestriction in Alnico 5 Magnet
- Alnico 5 ジシャク ニ オケル ジワイ
この論文をさがす
抄録
Magnetostrictions in Alnico 5 magnet were measured by means of a strain gauge. Magnetostriction remarkably depends on the direction of heat-treatment in magnetic field—tendency similar to that in other metals. Then by aging at 600°C, magnetostriction decreases on the whole at a direction perpendicular to the field of heat-treatment in magnetic field and in heat-treatment without magnetic field, and conversely, increases at a direction parallel to the field treatment. This is an interesting phenomenon for discussion of the structure of such materials. A faster cooling after fusion causes an increase in magnetostriction. The starting ponit of magnetostriction curve shifts to the side of lower magnetizing force, which is a property in soft magnetic material. In this state, powder patterns can be observed. A heating at 900°C, or a temperature between 1000° and 1200°C at which γ phase is produced, causes a magnetostriction curve distinctly different from that after heating at 950° or 1300°C which are solution temperatures.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 24 (12), 773-777, 1960
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458270080
-
- NII論文ID
- 130007333061
- 40018257604
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153044
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可