- “Giant” Chromium Intermetallic Compounds and Stress Corrosion Cracking in Al-Zn-Mg-Cu Alloys
- Al-Zn-Mg-Cu ゴウキン ニ オケル キョダイ クローム キンゾク カン カゴウブツ ニ ツイテ
- “Giant” Chromium Intermetallic Compounds and Stress Corrosion Cracking in Al-Zn-Mg-Cu Alloys
この論文をさがす
抄録
It is well known that very coarse crystals, up to 2 mm in length, found in large extrusions of 7075 alloy, have been identified as primary crystals of CrAl7 which grew under semi-continuous casting, and have caused the decrease in fatigue strength.<BR>Experiments were carried out to make a study of the prevention of the occurrence of “giant” chromium compounds without decreasing the resistance to stress corrosion cracking in Al-Zn-Mg-Cu alloys.<BR>The results obtained are as follows:<BR>(1) When the Cr content is less than 0.23% in Al-5.5%Zn-2.5%Mg-1.6%Cu alloy, the occurrence of “giant” chromium compounds is suppressed in commercial practice. However, the addition of >0.3%Mn, >0.3%Fe or >0.05%Ti promotes their occurrence.<BR>(2) The addition of Zr 0.1% has no influence on the occurrence of “giant” chromium compounds, and the addition of 0.2 to 0.3%Zr prevents their occurrence. It might be due to the increase in solubility of Cr in the Al-matrix caused by the formation of primary crystals of ZrAl3 before CrAl7 at a higher temperature.<BR>(3) It is concluded that Al-Zn-Mg-Cu alloy containing both 0.2%Cr and 0.1%Zr is a material having an excellent resistance to stress corrosion cracking, without fear of the occurrence of “giant” intermetallic compounds in industrial production.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 28 (2), 102-107, 1964
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458271232
-
- NII論文ID
- 40018258329
- 130007333063
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153769
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可