抄録
The tensile properties and microscopic structures were investigated with copper wires prepared from zone-refined ingot by 16 passes through the molten zones, by drawing of 99% reduction. The results obtained were as follows: (1) Large recrystallized grains were observed in the refined portions aged at room temperature, but no recrystallization was observed in the impurity-concentrated portions, crude copper, and commercial vacuum-melted copper. (2) According to the progress of recrystallization, remarkable reductions in ultimate tensile strength and micro-Vickers hardness values were also observed in the refined specimens aged at room temperature; these reductions are in clear relations with the decrease in the impurity content resulting from zone melting. (3) It has been found that the half-annealing time of the most refined specimen was much shorter than that of OFHC and almost similar to that of the spectroscopically pure copper (99.999%). Accordingly, the measurement of half annealing time may be one of the valuable methods to estimate the purity of copper.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 24 (11), 744-748, 1960
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458317952
-
- NII論文ID
- 130007333160
- 40018257597
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153037
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可