  • Study on the Gas-Carburizing Capacity of Some Practical Case-Hardened Steels
  • ゲンヨウハダショウコウ ノ ガス シンタンセイ ニ ツイテ

この論文をさがす

抄録

The gas-carburizing capacity of some case-hardened steels in common use (JIS-S 15 CK, SCM22 SNC 22, SNCM 21 and SNCM 23) was studied, using a batch-type gas furnace. Namely, the effect of dew point, carburizing temperature and holding time on the C distribution curve was determined by means of a turning method. From these results, the behavior of surface C content, the case depth and the diffusion coefficient of C due to various carburizing conditions was clarified concerning these kinds of steels. The main results obtained were as follows: (1) Cr-Mo steel showed a higher surface C content than Ni-Cr or Ni-Cr-Mo steels under the same gas conditions, and especially a much increased surface C content was observed in the former due to production of free cementite when the C potential of reaction gas rose over thes aturation content of C in austenite. On the other hand Ni-containing steels did not show such a tendency. (2) The case depth varied with changes in carburizing temperature, time, dew point and kinds of steels, but it will be noteworthy that the effect of dew point was particularly remarkable. (3) The diffusion coefficient of C at 925°C of these steels was 1300∼1700×10−5 cm2/day; within this range, that of Ni-containing steel was larger than that of Cr-Mo steel. (4) As the conclusion, the gas-carburizing capacity of case hardened steels are determined by C diffusivity and the behavior of surface C content from the view-point of kind of steels. That is, the steel with a larger C diffusivity and a comparatively high surface C content is effeciently carburized and the case depth becomes larger, under the same gas condition.

収録刊行物

  • 日本金属学会誌

    日本金属学会誌 24 (11), 727-731, 1960

    公益社団法人 日本金属学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ