- Properties of Zn-0.6Cu-0.10Ti Rod and Wire
- Zn-0.6 Cu-0.10 Ti ゴウキン ノ ボウ オヨビ センザイ ノ セイシツ ニ ツイテ
この論文をさがす
抄録
Mechanical properties of Zn-0.6Cu-0.10Ti rod and wire, fabricated by hot extruding and subsequently by cold rolling or drawing, were mainly investigated. The experimental results were as follows; (1) Tensile strength of the hot-extruded rod showed, independently of the extruding ratio, 26∼30 kg/mm2 which exceeded the value of rolled strip, but the tensile elongation and hardness were almost the same as those of the strip and the annealing temperature had a little effect on these properties. (2) When the rod was cold-reduced, the strength and hardness were decreased and the elongation was increased with increasing reduction. (3) The tensile strength and hardness of rod and wire were increased after low-temperature annealing, when the cold reduction exceeded about 75% for the tensile strength and about 50% for the hardness. And the almost same values as the extruded ones could be obtained by annealing of more than 90% reduction. (4) The most suitable annealing temperature to get the maximum strength for the highly cold-reduced wire was over the range from 150° to 200°C.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 28 (2), 86-90, 1964
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458323328
-
- NII論文ID
- 40018258333
- 130007333171
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153773
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可