- Study on the Mechanical Properties of 17·7 PH Stainless Steel Containing About 1%Al. (Study on 17·7 PH Stainless Steel, 4th Report)
- 約1%Alを含む17・7PH不銹鋼の冷間圧延材の機械的性質について
- ヤク 1 Al オ フクム 17 7PH フシュウコウ ノ レイカン アツエンザイ ノ キカイテキ セイシツ ニ ツイテ
- Study on the Mechanical Properties of 17·7 PH Stainless Steel Containing About 1%Al. (Study on 17·7 PH Stainless Steel, 4th Report)
この論文をさがす
抄録
17%Cr-7%Ni stainless steel containing 0.93%Al was experimented for determining its mechanical properties after several treatments such as solution treatment at 1050°C, 30∼70% cold-rolling and aging at 400∼500°C for 0.5∼500 hr. The following results were obtained: (1) Super-cooled austenite in this steel hardens due to internal stress and transformation into martensite by cold-rolling. The ratio of this hardening is larger than that of 18-8 stainless steel. (2) The hardness and the yielding strength of cold-rolled 17-7 PH steel increase exceedingly by aging at 400∼500° for suitable hours. (3) The highest mechanical properties of this steel were obtained under the following aging conditions; 400°C×100 hrs, 450°C×8∼12 hrs, 470°C×5∼8 hrs.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 24 (2), 96-100, 1960
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458374016
-
- NII論文ID
- 40018257638
- 130007333258
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153078
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可