The Dependence of Density, Electrical Resistivity, and Microstructure Upon the Process of Sintering in Fe-Al-Ni Magnet Alloy
Bibliographic Information
- Other Title
-
- Fe-Al-Ni焼結磁石の焼結過程に伴う密度,電気抵抗および組織の変化
- Fe-Al-Ni ショウケツ ジシャク ノ ショウケツ カテイ ニ トモナウ ミツド , デンキ テイコウ オヨビ ソシキ ノ ヘンカ
Search this article
Abstract
The process of sintering in FeAl2-Ni-Fe system (Al 12%, Ni 25%, Fe 63%) is discussed in this paper from the experimental stand-points; i.e. the dependence of various properties (density, electrical resistivity, microstructure) upon the sintering process of water-quenched specimens from their sintering temperature has been investigated. The conclusions obtained were as follows: (1) At the sintering temperature of 700°C, a decrease down to 1/26-1/58 of the green compacts in electrical resistivity at was already observed, suggesting that the diffusion of the components has set in . (2) When the sintering temperature reached 1250°C, rapid alloying of component particle, i.e. the reactions of FeAl2 phase+Ni phase→α′ phase, and α′ phase+Fe phase (γ)→α phase have been observed, and after sintering at 1350°C for 90 min the specimens consisted of α phase only. (3) The effect of compacting pressure upon the sintering process of the FeAl2-Ni-Fe system where no liquid phase is was existence has been found to be larger than that when a liquid phase was in existence. (4) The effect of sintering temperature upon the sintering process of the FeAl2-Ni-Fe system has been found to be larger than that of sintering time.
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 23 (4), 199-203, 1959
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390282681458532608
-
- NII Article ID
- 40018257403
- 130007333433
-
- NII Book ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL BIB ID
- 9152843
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed