- Effect of Cold Working on the Characteristics of a Ferromagnetic γ-Phase Alloy in the Co-Fe-Cr-Ni System (Anisotropy Induced by Cold Working in a Ferromagnetic γ-Phase Alloy in the Co-Fe-Cr-Ni System, Part 1)
- Co-Fe-Cr-Niケイ キョウジセイ ガンマ アイアイキン ノ トクセイ ニ オヨボス レイカン アツエン ノ エイキョウ ニ ツイテ
- Effect of Cold Working on the Characteristics of a Ferromagnetic γ-Phase Alloy in the Co-Fe-Cr-Ni System (Anisotropy Induced by Cold Working in a Ferromagnetic γ-Phase Alloy in the Co-Fe-Cr-Ni System, Part 1)
この論文をさがす
抄録
To determine the effect of γ\ ightleftharpoonsα transformation due to cold working upon the characteristics of a ferromagnetic γ-phase alloy, the thermal expansion, Young’s modulus and its temperature coefficient were measured on alloy specimens containing 27% of Co, 9% of Cr, 17% of Ni, and the rest Fe which were subjected to cold rolling to various reductions. It was found that the above characteristics were changed very much, showing anomalies caused by cold rolling. With subsequent heat treatment at various temperatures, anomalous changes of the characteristics occured at temperatures from 550° to 600°C, and recrystallization began at 700°C, resulting in a decrease of the anomalies. By observation of the microscopic structure and hardness tests, it was confirmed that the characteristics of the alloy were affected by the γ-α transformation due to cold working.
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 27 (4), 160-165, 1963
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282681458563840
-
- NII論文ID
- 40018258234
- 130007333498
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 9153674
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可